Effect of commercial silanes on bond strength of resin cement to lithium disilicate ceramic / Efeito de silanos comerciais na resistência de união do cimento resinoso à cerâmica de dissilicato de lítio

The aim of this study was to evaluate the effect of different commercial silanes on microshear bond strength of resin cement to lithium disilicate ceramic. Twenty ceramic samples with 10 mm in length, 10 mm wide and 3 mm in thickness were fabricated, etched with 10% hydrofluoric acid for 20 seconds, and divided into 5 groups, according to the commercial silane applied: G1- RelyX Ceramic Primer (3M ESPE), G2- Angelus Silane, G3- Prosil (FGM), G4- Dentsply Silane (Dentsply) and G5- Bis-Silane (Bisco). Silanes were applied in accordance to manufacturers' recommendations. Addition silicone molds with 1 mm in thickness, 10 mm in diameter and 3 perforations with 1 mm in diameter each one, were placed on ceramic and filled with the resin cement RelyX ARC (3M ESPE) in all groups. Light activation was performed with LED Bluephase G2 (Ivoclar Vivadent) at 1200 mW/cm2, for 30 seconds. Samples were maintained in 100% humidity at 37°C for 24 hours and submitted to microshear test. The data (MPa) were submitted to one-way ANOVA and Tukey test (α=0.05). The results obtained for each group were: G1: 22.39±2.99; G2: 23.35±4.08; G3: 26.05±5.46; G4: 18.56±4.09; G5: 25.26±4.10. Statistical analysis showed significantly lower microshear bond strength for G4. Fracture pattern analysis showed predominance of adhesive failures in G1 and G2. G3 and G5 presented higher percentage of cohesive failures in ceramic, and G4 showed mixed, adhesive and cohesive fractures with similar percentages. It was concluded that different silanes showed influence on the lithium disilicate ceramic ­ resin cement bond strength

O objetivo neste estudo foi avaliar o efeito de diferentes silanos comerciais na resistência de união ao microcisalhamento do cimento resinoso à cerâmica de dissilicato de lítio. Foram confeccionadas 20 amostras de cerâmica (10mm de comprimento, 10mm de largura e 3mm de espessura), condicionadas com ácido fluorídrico a 10% por 20 segundos e divididas em 5 grupos, de acordo com o silano aplicado: G1- RelyX Ceramic Primer (3M ESPE), G2- Silano Angelus, G3-Prosil (FGM), G4- Silano Dentsply e G5-Bis-Silane (Bisco). Matrizes de silicone por adição (1 mm de espessura, 10 mm de diâmetro e 3 perfurações com 1 mm de diâmetro) foram colocadas sobre a cerâmica e preenchidas com cimento resinoso RelyX ARC (3M ESPE). A fotoativação foi realizada com LED Bluephase G2 (Ivoclar Vivadent) a 1200 mW/cm2, por 30 segundos. As amostras foram mantidas em 100% de umidade a 37°C por 24 horas e submetidas ao teste de microcisalhamento. Os dados (MPa) (G1: 22,39+2,99; G2: 23,35+4,08; G3: 26,05+5,46; G4: 18,56+ 4,09; G5: 25,26+4,10) foram submetidos a análise de variância e ao teste de Tukey (p<0,05). A análise estatística mostrou valor de resistência de união significantemente menor para G4. A análise do padrão de fratura mostrou predominância de falha adesiva para G1 e G2. G3 e G5 apresentaram maior porcentagem de falha coesiva em cerâmica, e o G4 apresentou fraturas mista, adesiva e coesiva em igual porcentagem. Concluiu-se que os diferentes silanos apresentaram influência na resistência de união do cimento resinoso à cerâmica de dissilicato de lítio

Effect of Ceramic Interposition and Post-activation Times on Knoop Hardness of Different Shades of Resin Cement

Abstract The aim of this study was to evaluate Knoop hardness of different shades of a resin cement light-cured directly or through ceramic discs, measured 15 min or 24 h after light exposure, and at different depths. Specimens of a commercial resin cement (Variolink Veneer) in seven shades, were fabricated in an elastomeric mold, covered with a mylar strip, a 0.7 mm thick ceramic disc (IPS e.max Press) was placed and the cement was light-activated for 20 s using a blue LED (Radii-Cal). The cured resin cement specimens were transversely wet-flattened to their middle portion and microhardness (Knoop) values were recorded at 15 min after light exposure and after deionized water storage at 37 ºC for 24 h. Five indentations were made in the cross-sectional area at 100 and 700 μm depths from the top surface. Ten specimens were made for each test conditions. Data were submitted to ANOVA split-plot design (shade, post-cure time, mode of activation and depth), followed by Tukey post hoc test (α=0.05). Significant differences for shade (p<0.0001), mode of activation (p<0.001), post-cure time (p<0.0001) and depth (p<0.0001) were detected. No significant interactions (p>0.05) were found, except for shade x post-cure time (p<0.0045) and mode of activation x post-cure time (p<0.0003). Resin cement shade has a significant effect on Knoop hardness. Indirect activation through a ceramic material reduced significantly Knoop hardness. Hardness Knoop significantly increased after 24 h in all cements shades compared to values obtained after 15 min. Resin cement depth significantly reduced Knoop hardness.

Resumo O objetivo deste estudo foi avaliar a dureza Knoop de diferentes cores de um cimento resinoso fotoativado diretamente ou através da interposição de um disco de cerâmica, medindo 15 min ou 24 h após exposição à luz, em diferentes profundidades. Amostras do cimento resinoso (Variolink Veneer) em sete cores foram fabricados num molde de elastômero, coberto com tira de poliéster, seguido de um disco cerâmico (IPS e.max Press) com 0.7 mm de espessura e fotoativado por 20 s com o aparelho LED (IPS e.max Press). O cimento resinoso fotoativado foi transversalmente desgastado na porção média e os valores de microdureza Knoop foram obtidos após 15 min após exposição à luz e após armazenagem em água deionizada à 37 °C por 24 h. Cinco penetrações foram feitas na secção transversal à 100 e 700 μm da superfície de topo. Dez amostras foram confeccionadas para cada condição de teste. Os dados foram submetidos à Análise de Variância em esquema de parcelas subdivididas (cor, tempo pós-ativação, modo de ativação e profundidade), seguido pelo teste de Tukey post hoc (α=0,05). Diferença significante para a cor (p<0,0001), modo de ativação (p<0,001), tempo pós-ativação (p<0,0001) e profundidade (p<0,0001) foi detectada. Nenhuma interação significante foi encontrada (p>0,05), exceto para a interação cor x tempo pós-ativação (p<0,0045) e modo de ativação x tempo pós-ativação (p<0,0003). A cor do cimento resinoso teve significante efeito na dureza Knoop. A ativação indireta através do material cerâmico reduziu significativamente a dureza Knoop. A dureza Knoop aumentou significativamente após 24 h em todas as cores do cimento comparados aos valores obtidos após 15 min. A profundidade do cimento resinoso reduziu significativamente os valores de dureza Knoop.

Microtensile Bond Strength and Microhardness of Composite Resin Restorations Using a Sonic-Resin Placement System

Abstract The aim of this study was to evaluate the efficacy of applying sonic energy on microtensile bond strength and microhardness after the restoration process. A total of 40 human third molars were extracted. Class II cavities were prepared and restored with composite SonicFill or Filtek Z350 XT with and without the application of sonic energy. After the teeth were stored in water for 24 h, the teeth were sectioned into sticks (1.0 mm2) and subjected to tensile testing. For a depth Knoop hardness test, the samples were cut and indentations were made sequentially from the surface of the samples to the bottom of the samples in three intervals of 1 mm each. The samples were then subjected to a load of 50 g for 10 s. The results from the tensile (factors: placement system and composite) and hardness (factors: placement system, composite and depth) tests were subjected to the Kolmogorov-Smirnov normality test, followed by analysis of variance and Tukey's test (5% significance). For the placement system factor, higher bond strength was observed for the cavities that were restored with sonic energy (p < 0.001). For depth Knoop hardness, the hardness at 1 mm depth was significantly greater than that at 3 mm depth just for the restorations with Filtek Z350 XT composite without the application of sonic energy. Therefore, the use of sonic energy during the restorative process improved bonding, yet it did not markedly affect the depth hardness for both composites.

Resumo O objetivo deste estudo foi avaliar a eficácia da aplicação de energia sônica sobre a resistência de união à microtração e a microdureza após o processo de restauração. Um total de 40 terceiros molares humanos foram extraídos. Cavidades Classe II foram preparadas e restauradas com os compósitos SonicFill ou Filtek Z350 XT com e sem a aplicação de energia sônica. Após os dentes serem armazenados em água durante 24 h, foram seccionados em palitos (1,0 mm2) e submetidos a ensaio de tração. Para um ensaio de dureza Knoop de profundidade, as amostras foram cortadas e as penetrações foram feitas sequencialmente a partir da superfície para o fundo das amostras em três intervalos de 1 mm cada. As amostras foram então submetidas a uma carga de 50 g durante 10 s. Os resultados dos testes de tração (fatores: sistema de inserção e compósito) e dureza (fatores: sistema de inserção x compósito x profundidade) foram submetidos ao teste de normalidade Kolmogorov-Smirnov, seguido da análise de variância e do teste de Tukey (significância de 5%). Para o fator sistema de inserção, observou-se maior resistência de união para as cavidades que foram restauradas com energia sônica (p < 0,001). Para a dureza Knoop de profundidade, a dureza a 1 mm de profundidade foi significativamente maior do que a profundidade de 3 mm apenas para as restaurações com o compósito Filtek Z350 XT sem a aplicação de energia sônica. Portanto, o uso de energia sônica durante o processo restaurador melhorou a união, mas não afetou acentuadamente a dureza de profundidade para ambos os compósitos.

Effect of Metal Primers on Bond Strength of a Composite Resin to Nickel-Chrome Metal Alloy

Abstract This study evaluated the effects of three metal primers and one multi-mode adhesive system on the shear bond strength (SBS) of a flowable composite resin to nickel-chrome metal alloy (Ni-Cr). Ninety plates were cast from Ni-Cr and divided in nine groups (n=10). The surfaces were sandblasted with Al2O3 and primed with three adhesive primers: Alloy Primer (AP), Universal Primer (TP) and RelyX Ceramic Primer (CP), and a multi-mode adhesive (Scotchbond Universal, SU). The Adper Single Bond Plus (SB) and SU adhesives were also combined with adhesive primers. Control group did not have any surface treatment. The groups were: AP, AP+SB, AP+SU, TP+SB, TP+SU, CP+SB, CP+SU and SU. Composite cylinders were built on alloy surface. After 24 h, half the specimens were subjected to SBS and the other half to thermal cycling before testing. Data were analyzed by two-way ANOVA and Tukey’s test (a=0.05). Failure modes were assessed by SEM observation. Higher SBS were obtained with AP and TP combined with adhesives at 24 h and the lowest one for control group. Thermocycling reduced SBS for AP, CP+SU and SU. Combination between TP and SU resulted in the highest SBS after the thermocycling. TP groups showed all types of failures and high incidence of mixed failures. The use of AP and UP metal primers before application of SU and SB adhesive systems increased the SBS of composite to Ni-Cr. These combinations between metal primers and adhesives had the highest SBS after thermocycling.

Resumo Este estudo avaliou os efeitos de três primers para metais e um sistema adesivo multi-mode na resistência da união por cisalhamento (SBS) de um compósito resinoso de baixa viscosidade a uma liga niquel-cromo (Ni-Cr). Noventa placas Ni-Cr foram divididas em 9 grupos (n=10). As superfícies foram jateadas com Al2O3 e condicionadas com três primers adesivos: Alloy Primer (AP), Universal Primer (TP) e Rely X Ceramic Primer (CP) e um adesivo multi-mode (Scotchbond Universal, SU). Os adesivos Adper Single Bond Plus (SB) e SU foram combinados com os primers para metais. O grupo controle não recebeu nenhum tipo de tratamento superficial. Os grupos foram: AP, AP+SB, AP+SU, TP+SB, TP+SU, CP+SB, CP+SU e SU. Cilindros de resina foram construídos na superfície da liga. Após 24 h, metade dos espécimes foi submetido ao SBS, a outra metade foi termociclada previamente. Os dados foram analisados pelos testes ANOVA dois fatores e Tukey (a=0.05). Os tipos de fraturas foram determinados utilizando microscopia eletrônica de varredura (MEV). Os maiores valores de SBS foram obtidos com AP e TP combinados com adesivos após 24 h e o menor valor foi obtido no grupo controle. A ciclagem térmica reduziu a SBS para AP, CP+SU e SU. Combinação entre TP e SU resultou em altos valores de SBS após termociclagem. Os grupos TP apresentaram todos os modos de fratura e alta incidência de fraturas mistas. O uso dos primers AP e UP para metais antes da aplicação dos sistemas adesivos SU e SB aumentou a SBS entre o Ni-Cr e a resina composta. Essa combinação entre primers e adesivos mostrou os maiores valores de SBS após a termociclagem.

Influence of Water Storage and Bonding Material on Bond Strength of Metallic Brackets to Ceramic

Abstract: This study investigated the influence of water storage (24 h and 6 months), and Transbond XT and Fuji Ortho LC bonding materials on the bond strength of metallic brackets bonded to feldspathic ceramic. Four cylinders of feldspathic ceramic were etched with 10% hydrofluoric acid for 60 s. Each cylinder received two layers of silane. Metallic brackets were bonded to the cylinders using Transbond XT or Fuji Ortho LC. Light-activation was carried out with 40 s total exposure time using Bluephase G2. Half the specimens for each bonding materials (n=20) were stored in distilled water at 37 °C for 24 h and the other half for 6 months. Shear bond strength testing was performed after storage times at a crosshead speed of 1 mm/min. The adhesive remnant index (ARI) was used to evaluate the amount of adhesive remaining on the ceramic surface at ×8 magnification. Data were subjected to two-way ANOVA and Tukey's test (p<0.05). Transbond XT showed significantly higher bond strength (p<0.05) than Fuji Ortho LC. Significant differences in bond strength (p<0.05) were found when 24 h and 6 months storage times were compared between materials. ARI showed a predominance of score 0 for all groups, and higher scores at 1, 2 and 3 for 24 h storage time. In conclusion, storage time and bonding materials showed significant influence on the bond strength of brackets to ceramic.

Resumo: Este estudo investigou a influência da armazenagem em água (24 h e 6 meses) e dos materiais para colagem Transbond XT e Fuji Ortho LCO na resistência da união de bráquetes metálicos fixados a cerâmica feldspática. Quatro cilindros de cerâmica foram condicionados com ácido fluorídrico a 10% por 60 s. Todos os cilindros receberam duas camadas de silano. Bráquetes metálicos foram fixados aos cilindros utilizando os materiais Transbond XT ou Fuji Ortho LC. A fotoativação foi realizada com tempo de exposição total de 40 s utilizando Bluephase G2. Metade das amostras de cada material de colagem (n=20) foi armazenada em água destilada a 37 °C por 24 h e outra metade por 6 meses. O ensaio de resistência da união ao cisalhamento foi realizado após os períodos de armazenagem à velocidade de 1 mm/minuto. O Índice de Remanescente Adesivo (IRA) foi utilizado para avaliar a quantidade de adesivo residual na superfície da cerâmica, em lupa estereoscópica com aumento de 8x. Os dados foram submetidos à Análise de Variância de dois fatores e teste de Tukey (p<0,05). Transbond XT apresentou resistência de união significativamente maior do que Fuji Ortho LC. Diferença significante (p<0,05) na resistência da união foi encontrada entre os períodos de armazenagem, qualquer que fosse o material para colagem. O IRA mostrou predominância de escore 0 para todos os grupos, com aumento de escores 1, 2 e 3 para o período de armazenagem de 24 h. Em conclusão, o período de armazenagem e os materiais de colagem influenciaram significativamente a resistência da união de bráquetes à cerâmica.

Características relacionadas às propriedades dos elastômeros odontológicos: revisão / Particulars related to dental elastomer properties: review

O objetivo deste estudo foi realizar uma revisão da literatura sobre as características relacionadas às propriedades dos materiais elastômeros odontológicos. Os materiais de moldagem são utilizados em Odontologia para reprodução de detalhes anatômicos dos arcos dentários, em diferentes especialidades odontológicas, tais como: Planejamento e execução do tratamento ortodôntico, tratamentos reabilitadores na área da prótese com objetivo da confecção de modelos de estudo e de trabalho. Esta etapa da confecção de modelos convencionais e troquelizados é uma etapa importante para diversos procedimentos, podendo ser realizada com gesso a partir do molde. Para a obtenção de um modelo preciso com reprodução de detalhes e sem distorção, os materiais de moldagem devem ter alguns requisitos: fluidez suficiente para adaptação aos tecidos bucais; viscosidade suficiente para escoamento nas áreas a serem moldadas; polimerização (elastômeros) na cavidade bucal com tempo de presa adequado; após a polimerização, ausência de distorção ou rasgamento após remoção da boca; estabilidade dimensional até que o gesso seja vazado no molde; estabilidade dimensional do molde após remoção do modelo; e biocompatibilidade com os tecidos bucais. Contudo, de acordo com esta revisão de literatura, o fator de limitação não é o tipo de elastómero, mas a qualidade do gesso utilizado.

The aim of this study was to review in literature the characteristics of dental materials elastomers. The molding materials are used in dentistry for playing anatomical details of the dental arches in different dental specialties, such as planning and execution of orthodontic treatment, and rehabilitation treatments aimed at making study models. This stage of manufacture of models is an important step for many procedures, and can be performed in a cast from the mold. In order to obtain a precise model with detail reproduction and without distortion, some requisites are needed, such as sufficient fluidity to adapt to the oral tissues; viscosity to flow in the areas to be molded; polymerization at a suitable setting time while in the oral cavity. In addition, the materials must not distort or tear upon removal from the mouth; remain dimensionally stable until the plaster is poured into the mold; the model must maintain dimensional stability after removal from the mold, and allow second models to be constructed from the same impression, besides being biocompatible with the oral tissues. However, according to this literature review, the limiting factor is not the type of elastomer, but the quality of the plaster used.

Comparison of Silorane and Methacrylate-Based Composites on the Polymerization Heat Generated with Different Light-Curing Units and Dentin Thicknesses

This study evaluated the temperature variation in the pulp chamber during photoactivation of two restorative composite resins (Filtek P90 silorane-based composite and Heliomolar methacrylate-based composite) with either a quartz-tungsten-halogen (QTH) or light-emitting diodes (LED) light-curing unit (LCU) and using dentin thicknesses (0.5 and 1.0 mm). Standardized cavities (2x2x2 mm) were prepared in 80 bovine incisors, which were randomly assigned to 8 groups according to the photoactivation method and dentin thickness. Filtek P90 and Heliomolar (both in shade A3) were used with their respective adhesive systems (P90 self-etch primer / P90 adhesive bond and Excite adhesive). All experiments were carried out in a controlled environment (37°C). The temperature variations (°C) were recorded using a digital thermometer attached to a K-type thermocouple. The results were analyzed statistically by ANOVA and Tukey's test (α=0.05). For composite/dentin thickness interaction, temperature increase was significantly higher in 0.5 mm dentin thickness (40.07°C) compared with 1.0 mm dentin thickness (39.61°C) for Filtek P90. For composite/LCU interaction, the temperature increase was significantly higher for Filtek P90 (39.21°C - QTH and 40.47°C - LED) compared with Heliomolar (38.40°C - QTH and 39.30°C - LED). The silorane-based composite promoted higher temperature increase in the pulp chamber than the methacrylate-based composite.

Este estudo avaliou a variação de temperatura na câmara pulpar durante a fotoativação de duas resinas compostas (Filtek P90 – compósito à base de silorano e Heliomolar – compósito à base de metacrilato) com as unidades foto-ativadoras (UFs) luz de quartzo-tungstênio-halogênio (QTH) ou diodo emissor de luz (LED) e utilizando espessuras de dentina (0,5 e 1,0 mm). Cavidades padronizadas (2×2×2 mm) foram preparadas em 80 incisivos bovinos, as quais foram aleatoriamente divididas em 8 grupos de acordo com os métodos de fotoativação e espessura da dentina. Filtek P90 e Heliomolar (ambos na cor A3) foram utilizadas com seus respectivos sistemas adesivos (Primer P90 auto-condicionante / adesivo P90 e adesivo Excite). Todos os experimentos foram realizados em um ambiente controlado (37°C). As variações de temperatura (°C) foram mensuradas usando um termômetro digital conectado a um termopar tipo-K. Os resultados foram analisados estatisticamente por ANOVA e teste de Tukey (α=0,05). Para interação compósito/espessura de dentina, o aumento da temperatura foi estatisticamente superior para a espessura de dentina de 0,5 mm (40,07°C) quando comparado com a espessura de dentina de 1,0 mm (39,61°C) para a Filtek P90. Para a interação compósito/UFs, o aumento de temperatura foi estatisticamente superior para o Filtek P90 (39,21°C – QTH e 40,47°C – LED) quando comparado ao Heliomolar (38,40°C – QTH e 39,30°C – LED). Compósitos à base de silorano promovem maior aumento da temperatura na câmara pulpar em relação aos compósitos à base de metacrilato.

Influence of finishing/polishing on color stability and surface roughness of composites submitted to accelerated artificial aging.

Aim: To assess the influence of finishing/polishing procedure on color stability (ΔE ) and surface roughness (Ra ) of composites (Heliomolar and Tetric - color A2) submitted to accelerated artificial aging (AAA). Materials and Methods : Sixty test specimens were made of each composite (12 mm × 2 mm) and separated into six groups (n = 10), according to the type of finishing/polishing to which they were submitted: C, control; F, tip 3195 F; FF, tip 3195 FF; FP, tip 3195 F + diamond paste; FFP, tip 3195 FF + diamond paste; SF, Sof-Lex discs. After polishing, controlled by an electromechanical system, initial color (spectrophotometer PCB 6807 BYK GARDNER) and Ra (roughness meter Surfcorder SE 1700, cut-off 0.25 mm) readings were taken. Next, the test specimens were submitted to the AAA procedure (C-UV Comexim) for 384 hours, and at the end of this period, new color readings and R a were taken. Results: Statistical analysis [2-way analysis of variance (ANOVA), Bonferroni, P < 0.05] showed that all composites demonstrated ΔE alteration above the clinically acceptable limits, with the exception of Heliomolar composite in FP. The greatest ΔE alteration occurred for Tetric composite in SF (13.38 ± 2.10) statistically different from F and FF (P < 0.05). For Ra , Group F showed rougher samples than FF with statistically significant difference (P < 0.05). Conclusion: In spite of the surface differences, the different finishing/polishing procedures were not capable of providing color stability within the clinically acceptable limits.

Linear dimensional change, compressive strength and detail reproduction in type IV dental stone dried at room temperature and in a microwave oven

The type IV dental stone is widely used for the fabrication of dyes and master casts for fixed and removable partial prostheses. It is typically normal to wait at least 24 hours for the casts to dry prior to beginning the laboratory procedures. The waiting time has been shown to be greatly reduced by using microwave drying. OBJECTIVE: This study evaluated the influence of drying techniques at room temperature and microwave oven on the linear dimensional change, compressive strength and detail reproduction in type IV dental stones. MATERIAL AND METHODS: Three type IV dental stone brands were selected; elite Rock, Shera Premium and Durone IV. Two different drying protocols were tested in 4 groups (n=10); G1 - room temperature (25±4ºC) dried for 2 hours; G2 - room temperature dried for 24 hours; G3 - room temperature dried for 7 days and G4 - microwave oven dried at 800 W for 5 minutes and after 2 hours at room temperature. After drying, the samples were assayed for dimensional charges. The sample surface was submitted to the ImageTool 3.0 software for compressive strength in a universal testing machine with a cell load of 50 KN at a crosshead speed of 0.5 mm/minutes and the detail reproduction was analyzed with a stereomicroscope at 25x magnification. The statistical analysis of the linear dimensional change and compressive strength data were conducted by the ANOVA test followed by the Tukey test (p<0.05). Detailed reproduction values were reported in percentages. RESULTS: For the compressive strength test, Elite Rock and Durone IV did not present significant differences between G2 and G4, while Shera Premium did not present differences between G3 and G4. The best reproduction levels were observed for G3. CONCLUSIONS: Dental stone microwave oven drying showed a linear dimensional change similar to after room temperature drying for 24 hours and 7 days. The compressive strength of the stone dried in the microwave oven was similar to those dried at room temperature for 24 hours, with the exception of Shera Premium, which had similar results for microwave and room temperature drying for 7 days. For the microwave drying method the detail reproduction levels for samples dried at room temperature for 24 hours and 7 days were similar, except for the Durone IV.

Photoelastic evaluation of the effect of composite formulation on polymerization shrinkage stress

We compared polymerization stress in two commercial composites and three experimental composites made using camphorquinone (CQ) and/or phenylpropanedione (PPD) as photoinitiators. The internal surfaces of photoelastic resin discs with cylindrical cavities were roughened and treated with adhesive. Composites were divided into five groups: two commercial composites (Filtek Silorane and Filtek Z250) and three experimental composites with CQ/amine, CQ/PPD/amine, and PPD/amine. Composites were photopolymerized inside cavities, and subjected to photoelastic analysis immediately and at 24 hours and 7 days later using a plane polariscope. Stress created by Silorane (3.08 ± 0.09 MPa) was similar to that of Z250 (3.19 ± 0.13 MPa) immediately after photopolymerization (p > 0.05). After 24 hours and 7 days, Z250 (3.53 ± 0.15 and 3.69 ± 0.10 MPa, respectively) showed higher stress than Silorane (3.19 ± 0.10 and 3.16 ± 0.10 MPa, respectively). Qualitative analysis immediately after photopolymerization showed composite/CQ promoted higher stress than PPD, but stress levels at other evaluated times were statistically similar, varying between 3.45 ± 0.11 MPa and 3.92 ± 0.13 MPa. At 24 hours and 7 days, Silorane created the lowest stress. All photoinitiators created comparable tensions during polymerization.

Evaluation of the coefficient of thermal expansion of human and bovine dentin by thermomechanical analysis

The mismatch of thermal expansion and contraction between restorative materials and tooth may cause stresses at their interface, which may lead to microleakage. The present work compared the coefficient of thermal expansion (CTE) with the thermomechanical behavior of human and bovine teeth and determined if the CTE is a suitable parameter to describe tooth behavior. Fifteen human third molar and 15 bovine incisor tooth slices (6×5×2 mm) were allocated to 3 groups according to the test environment: G1 - room condition, G2 - 100 percent humidity, G3 - desiccated and tested in dry condition. Each specimen was weighed, heated from 20 to 70ºC at 10ºC min−1 and reweighed. The CTE was measured between 20 and 50ºC. Fresh dentin (human -0.49 percent ± 0.27, bovine -0.22 percent ± 0.16) contracted on heating under dry condition. Under wet conditions, only human teeth (-0.05 percent ± 0.04) showed contraction (bovine 0.00 percent ± 0.03) accompanied by a significantly lower (p<0.05) weight loss than in dry specimens (human 0.35 percent ± 0.15, bovine 0.45 percent ± 0.20). The desiccated dentin expanded on heating without obvious weight changes (0.00 percent ± 0.00). The CTE found was, respectively, in dry, wet and dissected conditions in ºC-1: human (-66.03×10-6, -6.82×10-6, 5.52×10-6) and bovine (-33.71×10-6, 5.47×10-6, 4.31×10-6). According to its wet condition, the dentin showed different CTEs. The thermal expansion behavior of human and bovine dentin was similar. A simple evaluation of the thermal expansion behavior of tooth structure by its CTE value may not be appropriate as a meaningful consideration of the effects on the tooth-material interface.

A discrepância entre a expansão e a contração térmica dos materiais restauradores e o dente podem causar estresse na sua interface, podendo levar a uma microinfiltração. O presente trabalho determinou e comparou o coeficiente de expansão térmica (CET) com o comportamento termo mecânico dos dentes humanos e bovinos e determinou se o CET é um parâmetro adequado para descrever o comportamento dental. 15 fatias (6×5×2 mm) de terceiros molares humanos e 15 de incisivos bovinos foram divididos em 3 grupos de acordo com o ambiente testado: G1 - condição ambiente, G2 - 100 por cento de umidade, G3 - dissecado e testado em condição seca. Cada espécime foi pesado, aquecido de 20 a 70C a 10ºC min-1 e pesados novamente. O CET foi mensurado entre 20 e 50ºC. Dentina fresca (humana -0,49 por cento ± 0,27, bovina -0,22 por cento ± 0,16) contrai no aquecimento sobre condição seca. Em condição úmida, somente dente humano (-0,05 por cento ± 0,04) mostrou contração (bovina 0,00 por cento ± 0,03) acompanhado por uma significante (p<0.05) perda de massa que os espécimes secos. A dentina dissecada expande no aquecimento sem mudanças óbvias de peso (0,00 por cento ± 0,00). O CET encontrado foi, respectivamente, em condições seca, úmida e dissecada em ºC-1: humana (-66,03×10-6, -6,82×10-6, 5,52×10-6) e bovina (-33,71×10-6, 5,47×10-6, 4,31×10-6). De acordo com sua condição de umidade, a dentina mostrou diferentes CETs. O comportamento de expansão térmica de dentes humanos e bovinos é similar. Uma simples avaliação do coeficiente de expansão térmica da estrutura dental pelo seu valor de CET pode não ser apropriada para uma consideração significativa dos efeitos na interface dente-material restaurador.

Shrinkage stress and degree of conversion of a dental composite submitted to different photoactivation protocols

The aim of this study was to evaluate the polymerization stress and degree of conversion of a composite submitted to different photoactivation protocols. The composite Filtek Z350 was placed in the central perforation of a photoelastic disc and polymerized using a LED-based curing unit (BluePhase II - IvoclarVivadent) with energy density of 12, 24 or 36 J/cm² using the following photopolymerization protocols: continuous high intensity (HI: 1200 mW/cm² during 10, 20 or 30s), continuous low intensity (LI: 650 mW/cm² during 18, 36 or 54s) and soft-start (SS: 150 mW/cm² during 5 s + 1200 mW/cm² during 9, 19 or 29s) (n=5). Photoelastic analysis was used to evaluate polymerization shrinkage stress and FTIR was performed to determine the degree of conversion of the composite. ANOVA 3-way procedure was used to determine the significance of the main effects and their interactions followed by two-way ANOVA for each time was performed (p<0.05). Shrinkage stress increased with higher values of energy. No statistically significant differences on polymerization shrinkage stress were found between high and low intensity activation modes. Softstart method generated stresses that were statistically lower than continuous modes except when 12 J/cm² was applied. Similar degree of conversion was observed for photoactivation modes used, except for soft-start mode with 12, 24 and 36 J/cm² that showed lowest levels of conversion. Energy density and activation mode influenced polymerization shrinkage stress, but no benefit on degree of conversion was observed.

O objetivo neste estudo foi avaliar a tensão de contração de polimerização e o grau de conversão de uma resina composta submetida a vários protocolos de fotoativação. O compósito Filtek Z350 foi inserido na perfuração central de um disco de resina fotoelástica e polimerizado usando uma unidade de fotoativação LED (BluePhase II - IvoclarVivadent) com as doses de energia de 12, 24 or 36 J/cm² usando os seguintes protocolos de polimerização: contínuo de alta intensidade (HI: 1200 mW/cm² durante 10, 20 ou 30s), contínuo de baixa intensidade (LI: 650 mW/cm² durante 18, 36 ou54s) e "soft-start" (SS: 150 mW/cm² durante 5 s + 1200 mW/cm² durante 9, 19 ou 29s) (n=5). Análise fotoelástica e Espectroscopia Infravermelha Transformada de Fourier (FTIR) foram usados para avaliar a tensão de contração de polimerização e grau de conversão do compósito respectivamente. O teste ANOVA três fatores foi usado para determinar os principais efeitos e interações das variáveis e seguidamente, ANOVA 2 fatores para ver a diferença entre os grupos (p<0.05). A tensão de contração aumentou com valores maiores de energia. Não foram observadas diferenças estatisticamente significantes para a tensão de contração entre os modos de alta e baixa intensidade. O modo "soft-start" gerou menor tensão que os modos contínuos, exceto quando 12 J/cm² foi aplicado. Similar grau de conversão foi observado para os modos de fotoativação usados, com exceção do modo "soft-start" com 12, 24 e 36 J/cm² que mostraram níveis menores de conversão. A dose de energia e modo de ativação influenciam a tensão de contração de polimerização, porém nenhum benefício no grau de conversão foi observado.

Avaliação do modo de ativação sobre a resistência à flexão e módulo de elasticidade de compósito restaurador com barras de diferentes formatos / Evaluation of activation modes on flexural strength and elastic modulusof a restorative composite testing bars with different shapes

Introdução e objetivo: O objetivo deste estudo foi avaliar a influência de dois modos de fotoativação sobre resistência à flexão e módulo de elasticidade de um compósito restaurador em dois formatos de barras. Materiais e método: Como controle (CO) foram confeccionadas dez barras seguindo a norma 4049/2000 da ISO (25 x 2 x 2 mm), fotoativadas em modo contínuo por 20s, e vinte barras experimentais com (comprimento x altura x largura) 7 x 1 x 2 mm foram confeccionadas e divididas em dois grupos G1 - fotoativação contínua por 20s e G2 - fotoativação por pulso tardio com ativação inicial de 2s e complementação de 18s após 5min. Após 24h da ativação, o teste foi realizado em uma máquina de ensaios com velocidade constante de 0,5 mm/min e monitorado pelo programa Blue Hill 2, que forneceu os valores de resistência à flexão (MPa) e módulo de elasticidade (GPa). Os valores foram sub-metidos à análise de variância de um fator e ao teste de Tukey (5%). Resultados: CO apresentou os maiores valores de resistência à flexão (158,6 ± 10,6) e módulo de elasticidade (12,20 ± 0,25), quando comparado a G1 (131,65 ± 21,2 e 9,28 ± 3,7) e G2 (131,1 ± 16,9 e 10,1 ± 4,4), que não apresentaram diferença significativa entre si. Conclusão: Foi possível concluir que a barra nas dimensões da ISO apresentou maiores valores de resistência à flexão e módulo de elasticidade que as barras experimentais e que os modos de ativação não influenciaram nas propriedades estudadas entre as barras experimentais.

Análise crítica do histórico e desenvolvimento das cerâmicas odontológicas / Critical analysis of the dental ceramics historical and development

O uso constante de restaurações estéticas na Odontologia tem promovido cada vez mais o desenvolvimento e o aperfeiçoamento de materiais que atendam a estes requisitos. As restaurações em cerâmica promoveram uma nova era estética e embora, este material restaurador tenha uma história antiga, a sua utilização clínica ainda é controversa. O avanço tecnológico, tanto no surgimento de novos materiais como no desenvolvimento de novas técnicas para a obtenção de resultados mais compatíveis com a dentição natural, tem estimulado cada vez mais o uso destes materiais. As cerâmicas odontológicas têm sido uma alternativa viável de tratamento protético tanto em áreas com perda de apenas um elemento dentário, quanto em áreas com perda de vários elementos. Esta revisão teve por objetivo realizar uma análise crítica a respeito dos diversos tipos de cerâmicas odontológicas utilizadas na confecção de restaurações protéticas indiretas, já que, cada vez mais novos materiais cerâmicos têm sido introduzidos no mercado durante as duas últimas décadas.

The constant use of aesthetic restorations in Dentistry has been promoting the development and the improvement of materials more and more to assist these requirements. Ceramic restorations have been promoted a new age in the aesthetic Dentistry, although, this restoring material has an old history and controversial clinical use. The aim of this review was to perform a critical analysis regarding the dental ceramics, for being a material thoroughly used for making of indirect restorations and still remains in technological development, because new ceramic materials have been introduced during the last two decades.

Effect of monomer content in the monomer-polymer ratio on complete denture teeth displacement

The purpose of the study was to verify the linear displacement of teeth in maxillary complete dentures influenced by different monomer-polymer ratios - according to the manufacturer's instructions, with 25 percent excess or 25 percent less monomer content - in the conventional and microwaved polymerization techniques. Wax base plates and wax planes were made on edentulous maxillary stone casts according to traditional method. The set was assembled in semi-adjustable articulator with a lower toothed stone cast as guide to mounting of the maxillary artificial teeth. Impressions were taken from this tooth arrangement with silicone and the mold was used to standardize the mounting of the teeth of all dentures. Referential points were made on the artificial teeth for linear measurements with optical microscope before processing of the dentures and after deflasking. Denture bases were conventionally packed with acrylic resin according to the monomer-polymer ratio protocol. Tooth displacement data were submitted to ANOVA and Tukey test (α=0.05). There were no statistically significant differences (p>0.05) between the group with monomer content recommended by the manufacturer and groups with 25 percent more and 25 percent less monomer, in both conventional and microwaved polymerizations. Excess or less monomer in the monomer-polymer ratio and polymerization types did not change the linear distance between teeth.

O propósito neste estudo foi verificar a movimentação linear de dentes em prótese total superior confeccionada com resina acrílica, proporcionada com conteúdo de monômero indicado pelo fabricante, com 25 por cento de excesso ou com 25 por cento a menos de monômero, nas técnicas de polimerização convencional e por microondas. Foram confeccionados 30 modelos, representando uma arcada maxilar desdentada com rebordo normal. As bases de prova e os planos de orientação foram confeccionados em cera e o conjunto montado em articulador semi-ajustável relacionado com um modelo inferior dentado. Depois da montagem dos dentes artificiais, a prótese foi moldada com silicone para duplicação das demais próteses. Foram confeccionados pontos referenciais para mensurações das distâncias entre os dentes, as quais foram analisadas com microscópio comparador linear antes e depois da desinclusão das próteses. As resinas acrílicas foram prensadas de modo convencional, alterando somente o conteúdo de monômero na proporção monômero-polímero recomendada pelo fabricante. Os dados da distância entre os dentes foram submetidos à análise de variância e ao teste de Tukey (5 por cento). Não houve diferença estatística entre os grupos com quantidade de monômero recomendada pelo fabricante e os grupos com 25 por cento a mais ou 25 por cento a menos de monômero, tanto na polimerização convencional como por microondas. A alteração do conteúdo de monômero e o tipo de polimerização (convencional ou por microondas) não exerceram influência na movimentação dental nas distâncias transversal e ântero-posterior.

Avaliação in vitro da deformação apical de canais de incisivos inferiores com achatamento mésio-distal submetidos à instrumentação manual e rotatória / In vitro evaluation of the apical deformation in the canal apex of mandibular incisors with mesio-distal flattening roots submitted to manual and rotatory instrumentation

OBJETIVO: O objetivo deste estudo foi avaliar in vitro a deformação apical, em raízes de incisivosinferiores com achatamento mésio-distal, submetidos à instrumentação manual e rotatória.MATERIAL E MÉTODO: Dez raízes foram separadas randomicamente em 2 grupos de 5elementos cada (n = 5) de acorado com o tipo de preparo. No Grupo I, as raízes tiveram seuscondutos inicialmente explorados com uma lima tipo K #15 e em seguida instrumentados até alima #35 pela técnica manual step-back. Durante o procedimento, os condutos foram irrigadoscom 1 ml de NaOCl a 1% a cada troca de instrumento. A obturação foi realizada com cimento deGrossman, pela técnica clássica. No Grupo II, o procedimento foi realizado utilizando-se o sistemarotatório ProfileTM. Os condutos também foram irrigados com 1 ml de NaOCl a 1% a cada trocade instrumento e obturados com cimento de Grossman, pela técnica clássica. Em seguida, efetuou-se um corte a 3 mm do ápice, obtendo-se corpos-de-prova com o mesmo comprimento, queforam levados ao microscópio óptico em aumento de 40 x para fotografia apical. As imagenscapturadas foram levadas a uma grade de integração elaborada especialmente para utilização emcomputador, permitindo analisar a área preenchida por guta-percha, cimento obturador e eventuaisespaços vazios. Os dados foram submetidos à análise estatística (Kruskal-Wallis), na qual foi verificado não haver diferença significante entre os grupos (p > 0,01). CONCLUSÃO: Concluiu-se que avariação no tipo de instrumentação dos condutos radiculares não promoveu deformação apical,não interferindo na obturação e no selamento hermético.

OBJECTIVE: The aim of the present study was to evaluate in vitro the apical deformation using different types of instrumentation. MATERIAL AND METHOD: Ten roots of mandibular incisors randomly divided into two groups of 5 roots each (n = 5) were used in the study. The working length was establisher by subtracting 1.0 mm from tooth total length. Group I : manual instrumentation using K-files (step-back), up to a #35 file; obturation with the Grossman sealer using the classical technique. Group II: rotatory instrumentation using ProfileTM System, obturation with Grossman sealer using the classical technique. 1 mm of each root was weared perpendicular to the long axis of the root exposing the obturation. The root end preparations were examined by optic microscope (40 x), coupled to a computer where the imagens were recorded. A grid was placed over to evaluate the guttapercha area, sealer area, and empty spaces. The sealer area and empty spaces were interpreted as suggestive of apical deformation. RESULTS: The data were submitted to nonparametric statistical analysis (Kruskal-Wallis), showing no statistical differences (p > 0.01) between Groups I and II.

Comparison of silorane and methacrylate-based composite resins on the curing light transmission

The aim of this study was to investigate the influence of different composite resins - Filtek P90 (silorane-based composite) and Heliomolar (methacrylate-based composite) - on light transmission and decrease in Knoop hardness between the bottom and top of cured specimens. The irradiance of a light-curing unit (LCU) was measured with a power meter (Ophir Optronics; 900 mw/cm2) and spectral distributions were obtained using a spectrometer (USB 2000). Twenty standardized cylindrical specimens (2 mm thick x 7 mm diameter) of each composite resin were obtained by curing using the LCU for 40 s. Light energy transmission through the composite was calculated (n=10). The Knoop hardness number for each surface was recorded as the mean of 3 indentations. The difference in Knoop hardness between the top and bottom (DKH) of the same specimen was calculated (n=10). The irradiance of light that passed through Filtek P90 (272 mW/cm2) was not significantly greater than that the passed through Heliomolar (271 mW/cm2). The DKH of Filtek P90 (25 percent) was significantly higher than that of Heliomolar (12 percent). There was a greater degree of subsurface polymerization of the methacrylate-based composite compared to the silorane-based composite.

O objetivo deste estudo foi avaliar a influência da diferença entre a dureza do topo e da base em compósitos restauradores. Foram utilizados os compósitos restauradores Filtek P90 (compósito à base de silorano) e Heliomolar (compósito à base de metacrilato). A irradiância da unidade foto-ativadodora (UF) foi mensurada com um potenciômetro Ophir Optronics (900 mw/cm2) e o espectro de luz foi obtido usando um espectrofotômetro (USB 2000). Vinte espécimes cilíndricos padronizados (2 mm de espessura por 7 mm de diâmetro) foram obtidos pela fotoativação utilizando UF (40 s) para cada compósito. A irradiância que passou através do compósito foi mensurada (n=10). O número de dureza Knoop para cada superfície foi calculado pela média de 3 penetrações. A diferença da dureza Knoop entre o topo e base (DDK) de um mesmo espécime foi calculada (n=10). A irradiância que passou através da Filtek P90 (272 mW/cm2) não foi estatisticamente superior a Heliomolar (271 mW/cm2). A DDK da Filtek P90 (25 por cento) foi estatisticamente superior a Heliomolar (12 por cento). O compósito a base de metacrilato apresentou melhor grau de polimerização na base quando comparado ao compósito à base de silorano.

Grau de conversão e densidade de ligações cruzadas de compósitos formulados com diferentes fotoiniciadores / Degree of conversion and cross-link density of resin composites formulated with different photoinitiators

O estudo verificou a influência da fonte de luz (FL) e do sistema fotoiniciador no grau de conversão (GC) e na densidade de ligações cruzadas (DLC) em compósitos com diferentes fotoiniciadores. Foram utilizadas as FLs XL2500® (3M/ESPE), Apollo95E® (DMD), UltraBlueIS® (DMC) e UltraLume5® (Ultradent), todas de acordo com as recomendações dos fabricantes e com 19J de energia aplicada, e os compósitos Pyramid-Bisco® (contendo fotoiniciador Lucirin TPO) e Filtek® Z250-3M/ESPE (fotoiniciador canforoquinona-CQ). O GC foi mensurado por espectroscopia de infra-vermelho transformada de Fourier. A DLC foi medida indiretamente por meio da leitura de dureza Knoop antes e após banho em etanol. Os dados foram submetidos à Anova e as médias, ao teste de Tukey (5%). Apollo 95E® produziu os maiores valores de GC para o compósito TPO (60,2%) quando a dose de energia foi mantida constante. A FL Ultra-BlueIS® não foi capaz de fotoativar o compósito TPO. Não existiram diferenças nos valores de GC para ocompósito CQ, a não ser quando Apollo 95E® foi usado pelo tempo recomendado pelo fabricante, levando a menor média (50,8%) de GC. Em geral, Ultra Lume5® produziu maior DLC, e Apollo 95E®, menor DLC para ocompósito TPO; para o compósito CQ não houve um padrão para os valores de DLC. Conclui-se que fontes de luz e fotoiniciadores influenciam as propriedades de compósitos dentais fotoativados.

Análise in vitro da deformação apical, variando-se o número de limas durante a instrumentação / In vitro analysis of the apical deformation, using a different number of files during the instrumentation

Introdução e objetivo: O objetivo deste estudo foi avaliar in vitro a deformação apical em raízes de incisivos inferiores curvos com achatamento mesiodistal, variando-se o número de limas durante a instrumentação dos condutos radiculares. Material e métodos: Separaram-se 20 raízes aleatoriamente em dois grupos (n = 10). No grupo I, as raízes tiveram seus condutos inicialmente explorados com uma lima tipo K #15 e em seguida instrumentados até a lima #35 pela técnica step-back. Durante o procedimento, os condutos foram irrigados com 1 mL de NaOCl a 1% a cada troca de instrumento. A obturação foi realizada com cimento de Grossman pela técnica clássica. No grupo II, o procedimento foi semelhante ao do grupo I, mudando apenas o número de limas durante a modelagem. Nesse grupo o instrumento de memória foi o #40. Em seguida cada raiz sofreu um desgaste apical de 1 mm com o propósito de expor a obturação, e realizou-se um corte a 3 mm do ápice, obtendo-se corpos-de-prova com o mesmo comprimento, os quais foram levados ao microscópio óptico em aumento de 40 x para fotografia apical. Analisaram-se as imagens capturadas por meio do software Image Tool, e a área ocupada pelo cimento obturador, pela guta-percha e por eventuais espaços vazios foi quantificada. Resultados: Os dados foram submetidos a análise estatística, em que se verificou não haver diferença significante entre os grupos I e II (p > 0.05). Conclusão: A variação no número de limas durante a instrumentação dos condutos radiculares não promoveu deformação apical, causando um selamento hermético semelhante entre os grupos estudados.

Introduction and objective: The aim of the present study was to evaluate in vitro the apical deformation in roots of crooked lower incisors with mesio-distal flattening, using a different number of files during the instrumentation. Material and methods: Twenty roots were randomly divided into two groups (n = 10). Group I: roots were initially instrumented with a K #15 file until a #35 file, through step-back technique. During instrumentation, the canals were irrigated with 1 mL of 1% NaOCl between every instrument change. Obturation was performed with Grossman sealer by lateral condensation technique. Group II: procedure was similar to group I, except for the files number, using file #40 as memory instrument. After that, each root was 1mm apical weared in order to reveal the filling. A 3 mm cut from the root apex was performed, resulting in samples with the same length, which were examined with an optical microscope (X40). The images captured by the Image Tool software were analyzed and the area occupied by sealer, gutta-percha and possible empty spaces was quantified. Results: Data was submitted to statistical analysis and showed no statistical significant differences between groups I and II (p > 0.05). Conclusion: The variation in the number of files during instrumentation did not promote apical deformation, but resulted in a similar hermetic sealing between the studied groups.